Adsorption and photocatalytic degradation of acetonitrile: FT-IR investigation
2003
Abstract The photocatalytic degradation of acetonitrile was carried out in liquid–solid regime in a batch reactor by using two types of commercial TiO 2 powders (Merck and Degussa P25) as photocatalysts. The concentration of acetonitrile and non-purgeable organic carbon (NPOC) were monitored. The initial rate of acetonitrile conversion was found higher on TiO 2 Merck than on TiO 2 P25. FT-IR spectroscopy was used to investigate the molecular features of the adsorption and photo-oxidation of acetonitrile on the two TiO 2 powders in a fully surface hydrated form. Acetonitrile was found adsorbed on Ti 4+ surface ions and hydroxyl groups for both types of TiO 2 . This interaction appeared fully…
Synthesis and physico-chemical characterization of Au/TiO2 nanostructures formed by novel "cold" and "hot" nanosoldering of Au and TiO2 nanoparticles…
2011
Abstract A novel approach to synthesize Au/TiO2 nanostructures with interesting optical properties is presented and discussed. It is based on the nanoparticle “cold” or “hot” nanosoldering occurring when two water suspensions of Au and TiO2 nanoparticles are merely mixed at room temperature or laser irradiated after mixing. Thanks to the high fraction and mutual reactivity of surface species, immediately after the mixing process, the encounters between Au and TiO2 nanoparticles in liquid phase are enough for “cold” nanosoldering of gold nanoparticles onto TiO2 nanoparticles to occur. The optical characterizations show that this fast process (timescale less than 1 min) is followed by a slowe…
Supermolecular control of charge transfer in dye-sensitized nanocrystalline TiO2 films: towards a quantitative structure-function relationship.
2005
Synthesis and immobilization of molecular switches onto titaniumdioxide nanowires
2009
Abstract The precursor [Fe III (L)Cl (L = N , N ′-bis(2′-hydroxy-3′-methyl-benzyliden)-1,7-diamino-4-azaheptane) is combined with [Mo(CN) 8 ] 4− yields a star shaped nona-nuclear cluster, [Mo IV {(CN)Fe III (L)} 8 ]Cl 4 . This Fe 8 Mo molecule is a high-spin system at room temperature. On cooling to 20 K some of the iron(III) centres in the molybdenum(IV)-star switch to the low-spin state as proven by Mossbauer spectroscopy. This molecule was deposited on TiO 2 nanowires by electrostatic interactions between the cluster cations and the surface functionalized titanium oxide nanowire. The synthesis and surface binding of the multistable molecular switch was demonstrated using IR and UV–Vis s…
Preparation in mild conditions of photocatalytically active nanostructured TiO2 rutile
2006
Abstract Nano structured TiO 2 rutile samples were prepared in mild conditions by hydrolysis of TiCl 4 in different solutions. The powders revealed a fair photoactivity for the photoeatalytic degradation of 4-nitrophenol. The influence of preparation procedure, pH and presence of Cl − and N 3 − anions on the physicochemical features and photocatalytic activity of the powders was investigated.
Red Shift in the Light Absorption Threshold of Anodic TiO2 Films Induced by Nitrogen Incorporation
2014
Abstract Titanium foils were anodized in ammonium containing and ammonium free solutions in order to check the possibility of inducing nitrogen incorporation into anodic TiO 2 films. XPS spectra confirmed the presence of O-Ti-N bonds on the surface of the anodic films prepared in ammonium biborate electrolytes. In order to evidence the effect of nitrogen incorporation on the light absorption threshold, photoelectrochemical behavior of as-anodized and high temperature annealed films as a function of the anodizing electrolyte composition were investigated. A photocurrent tail at energies lower than the mobility gap of TiO 2 appeared for those films prepared in ammonium containing electrolytes…
Osseointegration of one-piece zirconia implants compared with a titanium implant of identical design: a histomorphometric study in the dog
2010
Objective: The aim of this study was to evaluate osseointegration of one-piece zirconia vs. titanium implants depending on their insertion depth by histomorphometry. Material and methods: Four one-piece implants of identical geometry were inserted on each side of six mongrel dogs: (1) an uncoated zirconia implant, (2) a zirconia implant coated with a calcium-liberating titanium oxide coating, (3) a titanium implant and (4) an experimental implant made of a synthetic material (polyetheretherketone). In a split-mouth manner they were inserted in submerged and non-submerged gingival healing modes. After 4 months, dissected blocks were stained with toluidine blue in order to histologically asse…
Porous titania surfaces on titanium with hierarchical macro- and mesoporosities for enhancing cell adhesion, proliferation and mineralization
2014
Titanium received a macroporous titania surface layer by anodization, which contains open pores with average pore diameter around 5 μm. An additional mesoporous titania top layer following the contour of the macropores, of 100-200 nm thickness and with a pore diameter of 10nm, was formed by using the evaporation-induced self-assembly (EISA) method with titanium (IV) tetraethoxide as the precursor. A coherent laminar titania surface layer was thus obtained, creating a hierarchical macro- and mesoporous surface that was characterized by high-resolution electron microscopy. The interfacial bonding between the surface layers and the titanium matrix was characterized by the scratch test that con…
Pulsed Direct liquid Injection ALD of TiO2 Films Using Titanium Tetraisopropoxide Precursor
2013
Abstract TiO 2 thin films are grown by pulsed direct liquid injection atomic layer deposition with rapid thermal heating using titanium tetraisopropoxide and water vapor as precursors. The ALD growth rate is constant in the saturation zone range 35-47 ms at the temperature deposition of 280 °C. The TiO 2 growth rate of 0.018 nm/cycle was achieved in a self-limited ALD mode. SEM and AFM analysis showed the as-deposited films have a smooth surface with a low roughness. XPS analysis exhibited the stoichiometry of TiO 2 in the homogenous depth composition.